Inconel™713 has good creep strength, thermal fatigue performance and oxidation resistance below 900℃. The alloy ratio is simple, cobalt is excluded, and the density is reduced. It is usually used in the as-cast state. The use of hot isostatic pressing (HIP) treatment and subsequent heat treatment can improve plasticity and fatigue properties, and can also restore the structure and performance of parts that have degraded and reduced performance after long-term use. Long-term aging at 800°C will precipitate a small amount of σ phase, but it has no significant effect on performance. The alloy is suitable for manufacturing turbine rotor blades, guide blades, integral cast turbines and other high temperature parts of gas turbines operating below 900°C.

  Application field
• Manufacturing of turbine working blades, guide blades and integral cast turbines for aerospace, ground and offshore gas turbines that are widely used below 900°C
• Used extensively as diesel engine and gasoline engine turbocharger and hot extrusion die

Inconel™713 Chemical composition:
Fe ≤ 1.0
Mn ≤ 0.5
Si ≤ 0.5
S ≤ 0.01
P ≤ 0.015
Pb ≤ 0.001
Bi ≤ 0.0001
C ≤ 0.08-0.16
Cr ≤ 11.5-13.5
Mo ≤ 3.8-4.8
AI ≤ 5.5-6.4
Ti ≤ 0.5-1.0
B ≤ 0.008-0.020
Zr ≤ 0.06-0.15
Ni ≈ more than

We are a direct manufacturer. castings, pumps, and valves can be customized according to drawings. Our most advantageous specifications are greater than 5kg/piece, and there is no minimum minimum requirement. Users are welcome to try the order.

Our vacuum casting furnace capacity is: 50kg, 100kg, 1000kg.